Authors: Ben Ayed, R; Ajili, M; Garcia, JM; Ziouche, A; Kramer, JLC; Turki, NK
Article.
Optik. vol: 219. page: 0030-4026.
Date: OCT. 2020.
Doi: 10.1016/j.ijleo.2020.165303.
Abstract:
Undoped and Zn-doped Fe2O3 thin films were grown through spray pyrolysis. Zinc doping effect on the physical properties was investigated in detail. X-ray diffraction analysis confirms that all the Fe2O3 thin films showed a rhombohedral structure. The surface morphological study shows an interesting dendrite structure. The estimated band gaps energies were increased from 2.13 to 2.21 eV for indirect transition and from 1.80 to 1.85 eV for direct transition as function of doping ratio which was increased from 2 to 8 at. % Zn. The resistivity value (rho) of un-doped Fe2O3 thin film is 6.06 x 104 Omega. cm and as adding Zn ions, rho consequently decreased to 52 Omega. cm for 6 at. % Zndoped Fe2O3 thin films. Vibrating sample magnetometer (VSM) measurements showed an increase of the saturation magnetization with the Zn2+ insertion. Further, a ferromagnetic behavior was observed..